1.2. Cord from basalt roving (ShTB) 
Application:
Heat insulation and sound proofing of thermal equipment, filtration of aggressive conditions and corrosive gases. Also can be used as gasket element in heat exchangers, as resistant to acids and moisture reinforcement in composition materials.
Peculiarities of materials from basalt fiber: high chemical resistance to alkalis, acids and other aggressive conditions, low coefficient of thermal conductivity, high coefficient of sound proofing etc.
Properties (ShTB):
| Thermal conductivity, W/m °C |
| at 25°С | 0.050 |
| at 125°С | 0.080 |
| at 300°С | 0.092 |
| Dimensions, mm | Ø5 | 10x10 | 15x15 | 20x20 |
Rupture load, kgp (N),
not less | 100 (1000) | 130 (1300) | 220 (2200) | 350 (3500) |
| Nominal mass, g/m | 30 | 50 | 100 | 150 |
| Lengthening at rupture, %, not less | 30 | 35 | 40 | 45 |
| Working temperature, °C | 750 |
| Thickness, mm* | 8…50 |
| Width, mm* | 8…500 |
| Length, mm | unlimited |
* Cords dimensions can be changed according to Customer's request.
Cords from basalt roving are perfect substitutes for asbestos in thermal and friction machinery.
1.3. Cords from glass roving ShTS
Properties of ShTS: | | Thermal conductivity, W/m °C | | At 25°С | 0.048 | | Thermal shrinkage at 1000 °C, %, up to 450 | | Dimensions, mm | Ø4 | Ø8 | 12x12 | 16x16 | Rupture load, kgp (N),
not less | 20 (200) | 100 (1000) | 200 (2000) | 300 (3000) | | Nominal mass, g/m | 10 | 40 | 80 | 140 | | Lengthening at rupture, %, not less | 15 | 30 | 33 | 35 | | Working temperature, °C | до 450 | | Thickness, mm* | 8…50 | | Width, mm* | 8…500 | | Length, mm | unlimited |
|
* Cords dimensions can be changed according to Customer's request.
2. Cloth glassknitting erasering. LО-0.5.
The photo applies: as an average layer of three-layer honeycombing glassfibres. It is applies in airdesigns: flat, double, threefold curvature (facing of windows of the plane, detail of systems of an air conditioning, the cover капота, crests etc.) this is achieve decrease of weight of the design on 10-35 % at their sufficient rigidity.
Properties:
| Surface density, g/m2 | 400±40 |
| Thickness, mm (not less) than | 0.47 |
| Width of fold fabric, mm | 500 |
LО-1.0
 | Properties: | Surface density, g/m2 | 850±90 | | Thickness, mm (not less) than | 1.00 | | Width of fold fabric, mm | 600 |
|
3. FО-1.1. Properties:
| Surface density, g/m2 | 1100 |
| Thickness, mm (not less) than | 1,12 ±0,12 |
| Explosive loading at press by ball (not less) than | 588 |
Warp knitting OSSTP Combination warp knitting fabric from silica and polyamid yarn.
Application: it is a material for reinforcing element of a heat-shielding covering of space engineering.
Properties:
Width, mm 2500;
Thickness, mm 2.47;
Surface density, g/m 1700;
Braking load (not less than), kN 2700.
Warp knitting OKTM Combination warp knitting fabric from silica.
Application: it is a material for heat-shielding covering of space engineering.
Properties:
Width, mm 2200;
Thickness, mm 3.7±0.4;
Surface density, g/m2 2900±200;
Braking load (not less than), kN 3000
1200.
4. Unidirectional sleeves Ø70 mm, Ø100 mm, Ø120 mm containing glass or basalt roving in longitudinal direction 
Application: as a substitute roving of fabrics. As half finished product for a Photo of manufacture of the basalt fixture, at winding vessels of high pressure. Material are used at repair of pipelines (without trench way of repair).
Properties:
| linear density, g/m | 125 … 300; |
| Width of fold fabric, mm | 146 …785; |
| Thickness, mm | 0.35 …0.6; |
| Explosive loading: |
| - In a longitudinal direction | 100 ..1000; |
| - In a cross direction | 200 …2000 |
5. Knitted cloths from basalt roving 
Application: for the filtration of gases and aggressive liquids, as reinforcing, sound-proof material in composite materials.
Properties:
| surface density, g/m2 | 500…2000; |
| Thickness, mm | 0.5…6; |
| Width, mm | 1000 |